Cemented tungsten carbide brazed tips for adding wear resistance
Carbide tungsten carbide tip is also called tungsten carbide insert, which is made of high quality tungsten carbide + cobalt powder material mixed by formula and ratio through pressing and sintering, with high hardness, high strength and high wear resistance of an alloy material.Hard alloy cutter head has a series of excellent properties such as high hardness, wear resistance, good strength and toughness, heat resistance and corrosion resistance, especially its high hardness and wear resistance, even at 500℃ is basically unchanged, still has a high hardness at 1000℃.
Tungsten carbide has the characters of high wear resistance and good compressive properties, so it’s widely used in many different industries which requires high wear resistance. Especially in the agriculture industry, the machinery uses various kinds of wear parts, which are replaceable frequently. If the parts’ life time is longer, the cost will be much lower. More and more people are welding carbide tips to the casting parts, then the lifetime of the wear parts will be 5-10 times than the parts without carbide. All the carbide used in this industry we call it agricultural carbide
-- Easy to weld, no crack
-- Superior wear resistance
-- High hardness and strength
-- OEM & ODM are welcomed
-- Fast delivery and after-sale service timely
1, welding cutting carbide tiops structure should have enough rigidity
Sufficient rigidity is ensured by the maximum allowable external dimensions and by the use of high strength steel grades and heat treatments.
2, hard alloy blade should be fixed and reliable
The cemented carbide welding blade should have enough fixed firmness, which is guaranteed by the slot and welding quality, so the slot shape of the blade should be selected according to the shape of the blade and the geometrical parameters of the tool.
3, carefully check the knife rod.
Before welding the blade to the tool bar, necessary checks should be made on the blade and the tool bar, first of all, check that the supporting surface of the blade is not severely bent.The cemented carbide welding surface shall not have serious carburizing layer, and the dirt in the cemented carbide blade surface and tool bar insert groove shall be removed to ensure the welding is firm.
4, reasonable selection of solder
In order to ensure the welding strength, the appropriate solder should be selected.In the welding process, should ensure good wetting and fluidity, and eliminate bubbles, so that the welding and alloy welding surface full contact, no welding phenomenon.
5, the correct choice of welding flux
It is recommended to use industrial borax, which should be dehydrated in the drying oven before use, and then crushed, screened to remove mechanical debris, and then used.